Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL GTX™ Resin GTX987 - Asia - (PPE+PA*)-MF - Saudi Basic Industries Corporation (SABIC)

Check here, which other Noryl GTX datasheets, application examples or technical articles are available in Material Data Center

Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding - 機能

Any use of this information falls under the rules of our disclaimer.

商品の説明文

NORYL GTX™ 987 resin is a conductive, high performance non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade is optimized for primer-less electrostatic painting. NORYL GTX987 resin exhibits a low coefficient of thermal expansion (CTE) of ~7. This material is an excellent candidate for automotive applications such as body panels, tank flaps, and tailgates.

Processing/Physical Characteristics	値	単位	テスト基準
ISO データ
メルトボリュームレイト, MVR	7	cm³/10min	ISO 1133
温度	280	°C	-
荷重	5	kg	-
溶融時の密度	1080	kg/m³	-
溶融時の熱伝導率	0.21	W/(m K)	-
溶融時の比熱	1900	J/(kg K)	-
突き出し時の時の温度	223	°C	-
ASTM数据
メルトフローレイト, MFI	8.5	g/10min	ASTM D 1238
温度	280	°C	-
荷重	5	kg	-

機械的特性	値	単位	テスト基準
ISO データ
引張弾性率	3000	MPa	ISO 527
降伏応力	62	MPa	ISO 527
降伏ひずみ	5	%	ISO 527
破壊応力	62	MPa	ISO 527
破壊ひずみ	20	%	ISO 527
曲げ弾性率	2800	MPa	ISO 178
ノッチ付きシャルピー衝撃強さ, +23°C	11	kJ/m²	ISO 179/1eA
ノッチ付きアイゾット衝撃強さ, +23°C, 4mm	15	kJ/m²	ISO 180/1A
ノッチ付きアイゾット衝撃強さ, -30°C, 4mm	8	kJ/m²	ISO 180/1A
ASTM数据
引張弾性率	3250	MPa	ASTM D 638
降伏応力	55	MPa	ASTM D 638
破壊応力	55	MPa	ASTM D 638
降伏点伸び	5	%	ASTM D 638
破断伸び	15	%	ASTM D 638
曲げ弾性率	2700	MPa	ASTM D 790
ノッチ付きIzod衝撃強さ, 1/8 in	90	J/m	ASTM D 256
ノッチ付きIzod衝撃強さ, Low-Temperature	70	J/m	ASTM D 256
温度	-30	°C	-

熱的特性	値	単位	テスト基準
ISO データ
荷重たわみ温度, 0.45 MPa	190	°C	ISO 75-1/-2
ビカット軟化温度, B	198	°C	ISO 306
ビカット軟化温度, 120°C/h 50N	200	°C	ISO 306
線膨張係数, 平行	70	E-6/K	ISO 11359-1/-2
線膨張係数, 直角	75	E-6/K	ISO 11359-1/-2
ASTM数据
DTUL @ 66 psi	185	°C	ASTM D 648
ビカット軟化温度	192	°C	ASTM D 1525

その他の特性.	値	単位	テスト基準
吸水率.	3	%	Sim. to ISO 62
吸湿率	0.9	%	Sim. to ISO 62
密度.	1250	kg/m³	ISO 1183
密度	1250	kg/m³	ASTM D 792

Processing Recommendation Injection Molding	値	単位	テスト基準
Pre-drying - Temperature	100 - 110	°C	-
Pre-drying - Time	2 - 3	h	-
Processing humidity	≤0.02	%	-
樹脂温度	300 - 320	°C	-
金型温度	100 - 120	°C	-
Feed temperature	80 - 100	°C	-
Zone 1	260 - 280	°C	-
Zone 2	280 - 300	°C	-
Zone 3	300 - 320	°C	-

機能

特殊な特性

成形加工法.

射出成形.

領域別の利用可能性

アジア/太平洋地域.

Disclaimer

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com

Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.